CALIBRATED WIRE FOR COLD HEADING AND FORGING
QUALITY CONTROL OF WIRE PRODUCTION
|
|
Stainless steel (SAE / AISI)
| Steel grade | Diameter (mm) | process | Hardness (HV) | breaking strength (kg/mm2) |
Stretching (%) |
|---|---|---|---|---|---|
| 302HQ | less than 2.50 | BAIP | max. 150 | 48-63 | 40 min. |
| 2.51-2.85 | BAIP | max. 150 | 50-60 | 40 min. | |
| 2.86-3.40 | BAIP | max. 150 | 49-58 | 40 min. | |
| 3.41-3.70 | BAIP | max. 150 | 48-56 | 40 min. | |
| 3.71-4.30 | BAIP | max. 150 | 47-55 | 40 min. | |
| 4.31-4.90 | BAIP | max. 150 | 46-54 | 40 min. | |
| more than 2.50 | BAIP | max. 150 | 45-53 | 40 min. | |
| 304M | less than 3.00 | BAIP | max. 170 | 58-70 | 15 min. |
| 304M | more than 3.01 | BAIP | max. 170 | 54-65 | 15 min. |
| 304L | on demand | BAIP | max. 170 | 57-70 | 15 min. |
| 304HC | on demand | BAIP | max. 155 | max. 62 | 25 min. |
| 305J1 | less than 3.00 | BAIP | max. 155 | 53-65 | 35 min. |
| 3.01-3.50 | BAIP | max. 155 | 52-63 | 35 min. | |
| 3.51-4.00 | BAIP | max. 155 | 51-59 | 35 min. | |
| 4.01-4.50 | BAIP | max. 155 | 50-58 | 35 min. | |
| 4.51-5.00 | BAIP | max. 155 | 48-57 | 35 min. | |
| more than 5.01 | BAIP | max. 155 | 47-56 | 35 min. | |
| 316C | less than 3.00 | BAIP | max. 155 | 53-65 | 30 min. |
| 3.01-3.50 | BAIP | max. 155 | 52-63 | 30 min. | |
| 3.51-4.00 | BAIP | max. 155 | 51-62 | 30 min. | |
| 4.01-5.00 | BAIP | max. 155 | 50-60 | 30 min. | |
| more than 5.01 | BAIP | max. 155 | 49-58 | 30 min. | |
| 316L | on demand | BAIP | max. 145 | 53-63 | 32 min. |
| 410 | less than 3.00 | BAIP | max. 160 | 48-58 | 15 min. |
| 3.01-3.50 | BAIP | max. 160 | 47-57 | 15 min. | |
| 3.51-4.00 | BAIP | max. 160 | 46-56 | 15 min. | |
| more than 4.01 | BAIP | max. 160 | 45-55 | 15 min. | |
| 430 | less than 3.00 | BAIP | max. 170 | 47-57 | 20 min. |
| 3.01-3.50 | BAIP | max. 170 | 46-56 | 20 min. | |
| 3.51-4.00 | BAIP | max. 170 | 45-55 | 20 min. | |
| more than 4.01 | BAIP | max. 170 | 44-54 | 20 min. |
Carbon steel (SAE / AISI)
| Steel grade | Diameter (mm) | process | Hardness (HV) | breaking strength (kg/mm2) |
Stretching (%) |
|---|---|---|---|---|---|
| CH1A | on demand | LAIP | max. 130 | 32-42 | 15 min. |
| 1006AK | on demand | LAIP | max. 130 | 32-42 | 15 min. |
| 1008AK | on demand | LAIP | max. 130 | 32-42 | 15 min. |
| 1010AK | on demand | LAIP | max. 145 | max. 45 | 15 min. |
| 1012AK | on demand | LAIP | max. 145 | max. 46 | 15 min. |
| 1015AK | on demand | LAIP | max. 170 | 37-48 | 25 min. |
| 1018AK | less than 3.00 | LAIP | 140-180 | 45-56 | 25 min. |
| 1018AK | 3.01-4.00 | LAIP | 135-175 | 43-54 | 25 min. |
| 1018AK | more than 4.00 | LAIP | 130-170 | 41-51 | 25 min. |
| 1018AK | less than 3.00 | SAIP | 135-175 | 44-55 | 25 min. |
| 1018AK | 3.01-4.00 | SAIP | 130-165 | 42-53 | 25 min. |
| 1018AK | more than 4.00 | SAIP | 125-155 | 40-50 | 25 min. |
| 1022AK | less than 3.00 | LAIP | 145-185 | 46-57 | 25 min. |
| 1022AK | 3.01-4.00 | LAIP | 140-180 | 45-55 | 25 min. |
| 1022AK | more than 4.00 | LAIP | 130-170 | 40-52 | 25 min. |
| 1022AK | less than 3.00 | SAIP | 140-180 | 45-56 | 25 min. |
| 1022AK | 3.01-4.00 | SAIP | 135-170 | 44-54 | 25 min. |
| 1022AK | more than 4.00 | SAIP | 125-165 | 40-51 | 25 min. |
| 1022SK | on demand | SAIP | 140-185 | 43-58 | 20 min. |
| 10B21 | on demand | SAIP | 135-185 | 42-57 | 25 min. |
| 1541 | on demand | SAIP | 150-190 | 49-60 | 15 min. |
Alloy steel (SAE / AISI)
| Steel grade | Diameter (mm) | process | Hardness (HV) | breaking strength (kg/mm2) |
Stretching (%) |
|---|---|---|---|---|---|
| 4037 | on demand | SAIP | 140-190 | 45-58 | 15 max. |
| 35ACR | on demand | SAIP | 140-190 | 45-58 | 15 max. |
| 40ACR | on demand | SAIP | 140-190 | 45-58 | 15 max. |
| SCM435 | on demand | SAIP | 140-190 | 45-60 | 15 max. |
| SCM440 | on demand | SAIP | 140-190 | 45-60 | 15 max. |
| SCM453H | on demand | SAIP | 140-190 | 45-60 | 15 max. |
| SCM440H | on demand | SAIP | 140-190 | 45-60 | 15 max. |